# Savannah Resources Plc Metallurgical Testing Provides Further Positive Results

- Link: https://www.directorstalkinterviews.com/savannah-resources-plc-metallurgical-testing-provides-positive-results/412746711
- Published: 2018-03-05T07:09:18+00:00
- Author: Giles Arbor

**Savannah Resources plc** (LON:SAV), the AIM quoted resource development company,
has today announced that Phase 2 metallurgical test work has returned encouraging
results at the Mina do Barroso Lithium Project (‘Mina do Barroso’ or the ‘Project’),
located in Portugal (Figure 1). Further follow up work is now underway. To view 
the press release with the illustrative maps and diagrams please use the following
link: [Savannah RNS in Full](https://www.directorstalkinterviews.com/wp-content/uploads/2018/03/savannah.pdf)

**HIGHLIGHTS:**

· Analysis confirms high-grade spodumene mineralisation with a lithium content of
around 1.7% Li2O and low impurities – less than 0.5% Fe2O3

· Mineralogy analysis confirms spodumene is the dominant lithium mineral with low
contaminants

· Test work continues to confirm well proven, conventional metallurgical processes
will produce a spodumene concentrate

· Preliminary test work suggests that by using a process route combining both gravity
separation and flotation that a total recovery of at least 80% at a concentrate 
grade of over 6% Li2O is likely to be achieved

· Heavy Liquid Separation (HLS) testing and small-scale pilot testing confirms industry
benchmark, low-iron, 6% Li2O concentrate can be produced by low cost gravity processing

· Test work completed to date suggest at least 40% of the contained lithium can 
be recovered via gravity processing

· Preliminary tests show that over 70% of lithium not recovered by gravity can be
recovered by flotation at a grade of over 6% Li2O

· Further improvements are expected as part of Phase 3 of the test work programme
currently underway – diamond drilling is underway at Grandao and Reservatorio to
collect additional samples for the Phase 3 test programme, with results expected
in Q3 2018

· Mr Noel O’Brien, a metallurgist and lithium processing expert with over 35 years’
experience has been appointed as a technical consultant to direct Savannah’s metallurgical
test work programme

> **Savannah Resources CEO, David Archer said:** “We are delighted to see the results
> to date show that Mina do Barroso continues to demonstrate impressive metallurgical
> results, with spodumene being the dominant lithium mineral that can be recovered
> using conventional processing techniques to produce an industry benchmark product
> with low contaminants at good recoveries.
> “Mina do Barroso continues to shape up as a European near-analogue to the highly
> successful Western Australian spodumene producers. It is also important to remember
> that globally, ALL significant hard-rock lithium mines currently supplying the
> makers of lithium carbonate extract spodumene.
> “We hope that more metallurgical work will continue to refine and improve these
> already excellent results and we are delighted to welcome Noel O’Brien as a technical
> consultant to direct this programme.”

Figure 1. Mina do Barroso Project Summary Map showing prospects and drilling completed
to date

Summary of Phase 2 Metallurgical Test Work Programme and Results

The first series of testing involved conducting sighter tests on a combined sample
of mineralisation from Grandao, NOA and Reservatorio to establish metallurgical 
response and to determine the dominant lithium minerals.

The samples were crushed to 10mm, 6.3mm and 4mm and screened at 0.5mm. The crushed
samples were subjected to densimetric profiling tests using Heavy Liquid Separation(
HLS) at four densities of 2.9,2.8,2.7 and 2.6.

Each HLS SG fraction was examined by X-Ray Diffraction (“XRD”) to establish the 
dominant lithium minerals.

  |

Crush Size

  |

HLS Fractions

  |

Grade % Li_(2)O

  |

Grade % Fe_(2)0_(3)

  |

Mass % Distribution

  |

Li_(2)O % Distribution

  |

Spodumene Content

  |

Petalite Content

  |

Lepidolite Content

  |  
 |

10 mm

  |

2.9 product

2.9 middlings

2.8 middlings

2.7 residue

2.6 residue

  |

5.89

4.14

2.60

0.44

0.12

 

  |

0.37

0.32

0.36

0.27

0.13

  |

7.4

14.1

18.9

45.8

13.8

  |

25.3

33.7

28.4

11.6

1.0

  |

77%

51%

44%

8%

2%

  |

–

–

1%

–

1%

  |

1%

1%

1%

–

–

  |  
 |

6.3mm

  |

2.9 product

2.9 middlings

2.8 middlings

2.7 residue

2.6 residue

 

  |

6.00

4.22

2.54

0.41

0.12

  |

0.40

0.34

0.39

0.26

0.14

  |

8.1

13.0

16.3

47.2

15.4

  |

29.2

33.0

24.9

11.8

1.1

  |

79%

59%

38%

6%

2%

  |

–

–

–

–

–

 

  |

1%

1%

–

1%

–

  |  
 |

4  mm

  |

2.9 product

2.9 middlings

2.8 middlings

2.7 residue

2.6 residue

  |

6.19

4.26

2.56

0.40

0.11

  |

0.39

0.34

0.40

0.25

0.14

  |

10.2

11.9

13.7

47.0

17.3

  |

37.3

29.8

20.7

11.1

1.1

  |

78%

58%

37%

5%

–

  |

–

–

–

–

–

  |

1%

1%

1%

–

–

  |

 

These results are extremely encouraging and established the key attributes of:

· The dominant lithium mineral is spodumene. There is very little petalite and this
is confirmed by the low Li2O assays in the 2.7 and 2.6 float fractions. Petalite
is a light mineral that has a lower lithium content and if present, will show up
in these light fractions.

· The HLS results show improving lithium recovery and grades as the crush size decreases.
At a 4mm crush size, 37% of the lithium in the +0.5mm fraction has been recovered
at a grade of 6.19%.

· There are low impurities and an iron content in the spodumene of less than 0.5%
Fe2O3 which is well below the threshold of 1.4% Fe2O3 demanded by most off-takers.

· An overall head grade of 1.7% Li2O was obtained for the composite sample which
was higher than expected based on the past rock chip results

A second series of tests were conducted on a larger composite of the ore. This had
a head grade of 1.73% Li2O. Sub-samples were crushed to 4mm and 3.35mm and screened
at 0.5mm.

Samples were processed in a small-scale gravity DMS pilot plant that has a 100mm
cyclone.

The following results were obtained:

  |

Crush Size

  |

Medium SG

  |

Grade % Li_(2)O

  |

Grade % Fe_(2)O_(3)

  |

Mass% Distribution

  |

Li_(2)O % Distribution

  |  
 |

-4+0.5mm

  |

2.9 product

2.9 middlings

2.7 residue

  |

5.54

3.36

0.52

  |

0.40

0.35

0.23

  |

8.23

29.39

62.37

  |

26.28

55.20

18.52

  |  
 |

-3.35+ 0.5mm

  |

2.9 product

2.9 middlings

2.7 residue

  |

5.90

3.12

0.48

  |

0.72

0.36

0.21

  |

9.35

27.05

63.60

  |

32.43

49.64

17.93

  |

 

The concentrate from the 3.35mm test was subjected to magnetic separation to remove
iron minerals and residual mica. The grade of the concentrate increased to 6.03%
Li2O, with a loss of only 0.8% of the mass.

These results confirmed the findings of the HLS tests and indicated 30%-40% of the
lithium can be recovered by gravity as 6% concentrates. It also indicated that significant
mass rejection of low grade lithium residue of around 60% may be possible by using
up-front gravity separation.

This work is far from optimised and further improvements are expected.

The intermediate SG fractions (2.9 middlings), still contain 3%-4% Li2O and represent
around 50%-55% of the contained lithium. Further work is required to follow up on
the favourable phase 1 results to determine the best way to process this material
and improve the overall lithium recovery to over 80%.

Established methods are:

· Re-crushing of the middlings material and put it back through the DMS. This technique
has been successfully implemented by other operators.

· Investigate fines DMS which is a new technique that uses gravity separation down
to 0.3mm. The technology is advanced and one plant in Australia is about to install
a circuit.

· Use the well-established, conventional method of flotation to process fines. This
requires milling to less than 180 microns which is a well-established practice.

A preliminary un-optimised flotation test was done on the ore to determine whether
could be utilised to recover the lithium from the middlings material. At a grind
size of 180 microns, a very high figure of 71.4% of the lithium was recovered into
a mass yield of 31% at a grade of 6.04% Li2O.

This is a very encouraging result and moving forward, the use of flotation for further
lithium recovery and for feldspar recovery, will be studied in far greater depth.

Lithium Expert Joins the Savannah Technical Team

Mr Noel O’Brien has been appointed as a technical consultant to direct Savannah’s
metallurgical test work programme, he is a metallurgist and lithium processing expert
with over 35 years’ experience. Mr O’Brien is currently a technical adviser to Tawana
Resources Limited on its Bald Hill Lithium Project and Kidman Resources Limited 
on the Mount Holland Lithium Project. Previously, Mr O’Brien was a technical consultant
to the Galaxy Resources Lithium Project in Western Australia and the Bikita Minerals
Lithium Project in Zimbabwe.